Vitrified beads insulation mortar product introduction

Product Features (Expansion) Vitrified bead insulation mortar is made of vitrified microbeads lightweight aggregate as the main raw material, inorganic cementitious materials and a variety of admixtures are added, and the inorganic thermal insulation mortar prepared by premixing and dry mixing is used.

Product features are as follows:
Low thermal conductivity, good heat preservation effect Excellent heat insulation performance Sound insulation effect is good, can be used alone as sound insulation board Fire resistance is good: The material flammability is class A, can withstand high temperatures below 1000 degrees Celsius, make up for the existing organic thermal insulation material flammable high temperature Poison gas defects are the preferred products for interior insulation such as stairwells and fire escapes.
Good water resistance, low dry shrinkage, static leakage, strong shear and thixotropic properties, good workability, good resistance to freezing and thawing, stable performance, durable wind pressure resistance, good performance, and stable quality: giant power industry glass beads insulation mortar using industrial production , Optimize the ratio of raw materials, strictly control, and fundamentally ensure the consistency, stability and reliability of wood properties. Construction thickness is easy to control, construction adaptability, and high efficiency. As early as fast and dry, the process is simple and the construction period is greatly shortened.
The construction cost is low: the system is directly applied to the dry grass, the leveling layer and the insulation layer are combined into one, which greatly increases the construction cost.
The integrity is good: the insulation system and the base layer are fully bonded to form a continuous non-empty cavity to ensure the insulation layer is solid and safe, and the on-site construction can be freely shaped, and is especially used on shaped parts and inverted ceiling surfaces.
Green environmental protection: New inorganic materials, non-toxic and harmless, no radiation, is a true green environmental protection building materials, while creating value, it purifies the environment and has excellent social benefits.
Longer life: Due to excellent fire resistance, sound absorption, air permeability, water resistance and ice melting resistance, its weather resistance can reach 70 years, ensuring that the insulation system has the same life span as the base wall.

2. The scope of application is the outer insulation layer of the paint or tile; the outer plaster of the large-mode built-in Shule plate system.
Interior insulation of stairwells, partition walls, kitchens and toilets, enclosed balconies, ceilings, etc.;
Thermal insulation of steel structures;
Architectural special-shaped structural insulation;
Insulation filling of inner layer of dry hanging stone;
Ground insulation; floor heating insulation.
Upper roof, planting roof, wooden structure roof insulation 3. Product performance dry apparent density (kg/m3) ≤ 300
Thermal conductivity (W/m?K) ≤ 0.065
Wet apparent density (kg/m3)≤680
Linear shrinkage (%) ≤ 0.3
Compression strength (MPa)≥0.30
Tensile strength (MPa)≥0.15
Bonding strength (MPa)≥0.1
Softening coefficient ≥ 0.60
Coagulation time initial coagulation ≥ 1.0
Final coagulation ≤ 2.0
Heat storage system (xu4 re4 xi4) number (w/m2.k) ≥ 0.9

4. The construction process cleans the walls that require thermal insulation.
Add the appropriate amount of water to the vitrified bead dry mortar and stir well.
According to design requirements, the insulation thickness shall be no less than one per square meter with a well-stirred insulation paste.
Apply the insulation layer 2-3 times to complete. The first pass requires that every effort be made to compact it so that it adheres firmly to the wall and tries its best to make it thick. After 3-4 hours of curing and dryness, apply 2-3 times and level the calender.
Dividing sinks should be embedded directly in the insulation during the second pass.
After the insulation layer is substantially dry, it is pasted with a grid cloth or a steel wire mesh (within the outer wall insulation, no mesh cloth is required).

5. Precautions The construction temperature should not be lower than 5°C, and the insulation layer should be cured and dried for about 2 days (appropriate for the palm of the hand), and then the construction of the protective surface layer is performed.
The well-mixed insulation slurry must be used within 1 hour. Use of outdated ash is prohibited.

6. Stored in a ventilated, dry condition for 8 months, protected from rain, moisture, and sun.